Coppers range of advantageous characteristics a quite well known including high electrical and thermal conductivity, excellent corrosion resistance to name but a few.
Dispersion strengthened coppers add the advantage of higher strengths which means they can be used for a range or applications such as welding consumables.
Copper (Cu) is a widely used metal due to the advantages of high electrical and thermal conductivities, outstanding corrosion resistance and ease of production. However, in the pure form, mechanical properties of copper deteriorate dramatically at elevated temperature conditions. Based on the existing need for materials which possess high thermal conductivity coupled with high strength and also provide resistance to softening and degradation, different copper alloys have been developed. In order to increase strength of copper at high temperatures, precipitation hardening and oxide dispersion strengthening or both of these mechanisms can be used.
GLIDCOP AL-60 (C15760) is primarily designed for applications requiring the highest elevated temperature strength coupled with relatively high electrical and thermal conductivities. It exhibits a high degree of resistance to softening after exposure to elevated temperatures. GLIDCOP AL-60 has sufficient cold working characteristics for heading, extrusion and some drawing and rolling operations.
- Resistance welding electrodes
- Solder gun tips and MIG contact tips
- Welding electrodes made from GLIDCOP exhibit improved life
- Good non-sticking performance on coated steels
GLIDCOP AL-60 is designated in UNS as C15760.
Table 1: Mechanical properties – Typical room temperature properties of GLIDCOP® AL-60
Figure 1: Hardness vs. Temperature for some Copper alloys: DSC-Dispersion Strengthened Copper; DHP-Deoxidized High Phosphorus Coper, DSC-TiC-Dispersion Strengthened copper with Titanium Carbide
Figure 2: Contact tip conductivity comparison at 20°C: Copper Silver (CuAg); Deoxidized High Phosphorus Copper (DHP); Copper Chrome Zirconium (CuCrZr); (Dispersion Strengthened Copper, (DSC); Dispersion Strengthened Copper w/ Titanium Carbide
Structural stability of the both as-extruded materials after 1h annealing in H2 at 200 to 900°C was tested by light microscopy, (see Figure 3) and also indirectly, by means of the Brinell hardness (see Figure 4). The Cu–MgO composite hardness is only 90 HB, and falls down above 200°C as a result of the softening due to the recrystallization and abnormal grain growth. Figure 3a documents a typical fully recrystallized microstructure. On the other hand, the very good initial Cu–Al2O3 hardness of 160 HB exhibits no/minor hardness changes after the annealing and cooling to room temperature, Figure 4, thus suggesting an excellent thermal stability of the microstructure. The Cu–Al2O3 microstructure after 1h annealing at 900°C depicted in Figure 3b shows that in the material have took place recrystallization processes but newly formed grains have remained in ultra-fine sizes due to the effective Al2O3 dispersoids.
Figure 3: Light micrographs of the as-annealed microstructures: (a) Cu–MgO after annealing at 600°C for 1h in H2; (b) Cu–Al2O3 after annealing at 900°C for 1h in H2
Figure 4: The Brinell hardness versus annealing temperature for the Cu–Al2O3 and Cu–MgO materials
1. O.Dinçer, M.Kaan Pehlivanoglu, A.F.Dericioglu: High strength copper alloys for extreme temperature conditions, 18. Uluslararası Metalurji ve Malzeme Kongresi, IMMC 2016, p.693-696, Accessed July 2017;
2. GLIDCOP® Dispersion Strengthened Copper, Accessed 7 July 2017;
3. LUVATA, Accessed July 2017;
4. J. Ďurišin, K.Ďurišinova, M.Orolínová: Thermal stability of nanostructure of dispersion strengthened copper alloys, METAL 2015, Jun 3rd-5th, 2015, Brno, Czech Republic, EU.
Date Published: Jun-2018